λ-MnO2 Thin Films with Sponge-Like Structures: Synthesis, Characterization and Physiochemical Applications

https://doi.org/10.22146/ijc.64392

Khalid Abdelazez Mohamed Ahmed(1*)

(1) Department of Chemistry, Faculty of Science and Technology, Al-Neelain University, P.O. Box 12702, Khartoum, Sudan; Department of Chemistry, University College - Khurma, Taif University, P.O. Box 11099, Taif 21944, Saudi Arabia
(*) Corresponding Author

Abstract


Manganese dioxide has acquired significant research attentiveness in many fields over the past years because of its exciting physicochemical features. The magnetized λ-MnO2 thin films with sponge-like structures (TSLs) were prepared by hydrothermal-soft chemical and delithiation-lithium manganese process. The XRD, XPS, EDX, FESEM, TEM, HR-TEM, and N2 adsorption-desorption techniques were used to characterize the as-prepared product’s structure composition, morphology, and surface area. The particle growth details of λ-MnO2 are postulated by the oxidation-ionic change-delithiation (OID) mechanism. The electrochemical property was analyzed by galvanostatic discharge-charging, electrochemical impedance spectrum (EIS), and cyclic voltammetry (CV). Special attention of λ-MnO2 S.L.s is given to their applications in the degradation of methyl orange (MO) from wastewater under O2 air bubble pump and cathodic substance in the lithium-ion battery. Due to the peculiarity crystal form and morphology face, the λ-MnO2 TSLs might be promisingly applied in the various physicochemical area.

Keywords


manganese dioxide; sponges-like; cathode; methyl orange

Full Text:

Full Text PDF


References

[1] Shan, R., Lu, L., Gu, J., Zhang, Y., Yuan, H., Chen, Y., and Luo, B., 2020, Photocatalytic degradation of methyl orange by Ag/TiO2/biochar composite catalysts in aqueous solutions, Mater. Sci. Semicond. Process.,114, 105088.

[2] Khan, R., Hassan, M.S., Cho, H.S., Polyakov, A.Y., Khil, M.S., and Lee, I.H., 2014, Facile low-temperature synthesis of ZnO nanopyramid and its application to photocatalytic degradation of methyl orange dye under UV irradiation, Mater. Lett., 133, 224–227.

[3] Shen, Y., Wang, W., and Xiao, K., 2016, Synthesis of three-dimensional carbon felt supported TiO2 monoliths for photocatalytic degradation of methyl orange, J. Environ. Chem. Eng., 4 (1), 1259–1266.

[4] Basahel, S.N., Ali, T.T., Mokhtar, M., and Narasimharao, K., 2015, Influence of crystal structure of nanosized ZrO2 on photocatalytic degradation of methyl orange, Nanoscale Res. Lett., 10 (1), 73.

[5] Zheng, Q., and Lee, C., 2014, Visible light photoelectrocatalytic degradation of methyl orange using anodized nanoporous WO3, Electrochim. Acta, 115, 140–145.

[6] Zhang, K., Kim, D., Hu, Z., Park, M., Noh, G., Yang, Y., Zhang, J., Lau, V.W., Chou, S.L., Cho, M., Choi, S.Y., and Kang, Y.M., 2019, Manganese based layered oxides with modulated electronic and thermodynamic properties for sodium ion batteries, Nat. Commun., 19, 5203–5215.

[7] Misnon, I.I., Aziz, R.A., Zain, N.K.M., Vidhyadharan, B., Krishnan, S.G., and Jose, R., 2014, High performance MnO2 nanoflower electrode and the relationship between solvated ion size and specific capacitance in highly conductive electrolytes, Mater. Res. Bull., 57. 221–230.

[8] Lao-atiman, W., Julaphatachote, T., Boonmongkolras, P., and Kheawhom, S., 2017, Printed transparent thin film Zn-MnO2 battery, J. Electrochem. Soc., 164 (4), A859.

[9] Suren, S., and Kheawhomm, S., 2016, Development of a high energy density flexible zinc-air battery, J. Electrochem. Soc., 163 (6), A846.

[10] Khamsanga, S., Pornprasertsuk, R., Yonezawa, T., Mohamad, A.A., and Kheawhom, S., 2019, δ-MnO2 nanoflower/graphite cathode for rechargeable aqueous zinc ion batteries, Sci. Rep., 9 (1), 8441.

[11] Lee., S., Nam, G., Sun, J., Lee, J.S., Lee, H.W., Chen, W., Cho, J., and Cui, Y., 2016, Enhanced intrinsic catalytic activity of λ-MnO2 by electrochemical tuning and oxygen vacancy generation, Angew. Chem. Int. Ed., 55 (30), 8459–8765.

[12] Musil, M., Choi, B., and Tsutsumi, A., 2016, λ-MnO2 positive electrode for fuel cell/battery systems, J. Electrochem. Soc., 163, A2047.

[13] Xue, Y., Chen, Y., Zhang, M.L., and Yan, Y.D., 2008, A new asymmetric supercapacitor based on λ-MnO2 and activated carbon electrodes, Mater. Lett., 62, 3884–3886.

[14] Li, L., Qu, W., Liu, F., Zhao, T., Zhang, X., Chen, R., and Wu, F., 2014, Surface modification of spinel λ-MnO2 and its lithium adsorption properties from spent lithium ion batteries, Appl. Surf. Sci., 315, 59–65.

[15] Yuan, C., Zhang, Y., Pan, Y., Liu, X., Wang, G., and Cao, D., 2014, Investigation of the intercalation of polyvalent cations (Mg2+, Zn2+) into λ-MnO2 for rechargeable aqueous battery, Electrochim. Acta, 116, 404–412.

[16] Robinson, D.M., Go, Y.B., Greenblatt, M., and Dismukes, G.C., 2010, Water oxidation by λ-MnO2: Catalysis by the cubical Mn4O4 subcluster obtained by delithiation of spinel LiMn2O4, J. Am. Chem. Soc., 132 (33), 11467–11469.

[17] Liu, N., Mohanapriya, K., Pan, J., Hu, Y., Sun, Y., and Liu, X., 2020, A facile preparation of λ-MnO2 as cathode material for high-performance zinc-manganese redox flow battery, J. Electrochem. Soc., 167 (4), 040517.

[18] Chen, W., Zhan, X., Luo, B., Ou, Z., Shih, P.C., Yao, L., Pidaparthy, S., Patra, A., An, H., Braun, P.V., Stephens, R.M., Yang, H., Zuo, J.M., and Chen, Q., 2019, Effects of particle size on Mg2+ ion intercalation into λ-MnO2 cathode materials, Nano Lett., 19 (7), 4712–4720.

[19] Khan, I., Saeed, K., and Khan, I., 2019, Nanoparticles: Properties, applications and toxicities, Arabian J. Chem., 12 (7), 908–931.

[20] Ahmed, K.A.M., Zeng, Q., Wu, K., and Huang, K., 2010, Mn3O4 nanoplates and nanoparticles: Synthesis, characterization, electrochemical and catalytic properties, J. Solid State Chem., 183 (3), 744–751.

[21] Ahmed, K.A.M., Abbood, H.A., and Huang, K., 2012, Hydrothermal synthesis of Mn(OH)O nanowires and their thermal conversion to (1D)-manganese oxides nanostructures, J. Cryst. Growth, 358, 33–37.

[22] Tang, W., Shan, X., Li, S., Liu, H., Wu, X., and Chen, Y., 2014, Sol-gel process for the synthesis of ultrafine MnO2 nanowires and nanorods, Mater. Lett., 132, 317–321.

[23] Shen, M., Wang, Y., and Zhang, Y.X., 2020, Neatly arranged mesoporous MnO2 nanotubes with oxygen vacancies for electrochemical energy storage, Dalton Trans., 49 (48), 17552–17558.

[24] Zheng, D., Sun, S., Fan, W., Yu, H., Fan, C., Cao, G., Yin, Z., and Song, X., 2005, One-Step Preparation of single crystalline β-MnO2 nanotubes, J. Phys. Chem. B, 109 (34), 16439–16443.

[25] Xu, K., Li, S., Yang, J., and Hu, J., 2018, Hierarchical hollow MnO2 nanofibers with enhanced supercapacitor performance, J. Colloid Interface Sci., 513, 448–454.

[26] Zhao, L., Yu, J., Li, W., Wang, S., Dai, C., Wu, J., Bai, X., and Zhi, C., 2014, Honeycomb porous MnO2 nanofibers assembled from radially grown nanosheets for aqueous supercapacitors with high working voltage and energy density, Nano Energy, 4, 39–48.

[27] Greedan, J.E., Raju, N.P., Wills, A.S., Morin, C., Shaw, S.M., and Reimers, J.N., 1998, Structure and magnetism in λ-MnO2 geometric frustration in a defect spinel, Chem. Mater., 10 (10), 3058–3067.

[28] Wang, N., Cao, X., Lin, G., and Shih, Y., 2007, λ-MnO2 nanodisks and their magnetic properties, Nanotechnology, 18, 475605–475608.

[29] Kim, S., Lee, J., Kang, J.S., Jo, K., Kim, S., Sung, Y.E., and Yoon, J., 2015, Lithium recovery from brine using a λ-MnO2/activated carbon hybrid supercapacitor system, Chemosphere, 125, 50–56.

[30] Kim, S., Kang, J.S., Joo, H., Sung, Y.E., and Yoon, J., 2020, Understanding the behaviors of λ-MnO2 in electrochemical lithium recovery: Key limiting factors and a route to the enhanced performance, Environ. Sci. Technol., 54 (14), 9044–9051.

[31] Yuan, Y., and Cheng, L. 2012, Theoretical prediction for the structures of gas phase lithium oxide clusters: (Li2O)n (n = 1–8), Int. J. Quantum Chem., 113 (9), 1264–1271.

[32] Nasrollahzadeh, M.S., Hadavifar, M., Ghasemi, S.S., and Chamjangali, M.A., 2018, Synthesis of ZnO nanostructure using activated carbon for photocatalytic degradation of methyl orange from aqueous solutions, Appl. Water Sci., 8 (4), 104.

[33] Xia, H., Xiao, W., Lai, M.O., and Lu, L., 2009, Facile synthesis of novel nanostructured MnO2 thin films and their application in supercapacitors, Nanoscale Res. Lett., 4 (9), 1035.

[34] Ahmed, K.A.M., Peng, H., Wu, K., and Huang, K., 2011, Hydrothermal preparation of nanostructured manganese oxides (MnOx) and their electrochemical and photocatalytic properties, Chem. Eng. J., 172 (1), 531–539.

[35] Yao, Y., Cai, Y., Wu, G., Wei, F., Li, X., Chen, H., and Wang, S., 2015, Sulfate radicals induced from peroxymonosulfate by cobalt manganese oxides (CoxMn3−xO4) for Fenton-like reaction in water, J. Hazard. Mater., 296, 128–137.

[36] Luo, S., Duan, L., Sun, B., Wei, M., Li, X., and Xu, A., 2015, Manganese oxide octahedral molecular sieve (OMS-2) as an effective catalyst for degradation of organic dyes in aqueous solutions in the presence of peroxymonosulfate, Appl. Catal., B, 164, 92–99.



DOI: https://doi.org/10.22146/ijc.64392

Article Metrics

Abstract views : 2393 | views : 1758


Copyright (c) 2021 Indonesian Journal of Chemistry

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

 

Indonesian Journal of Chemistry (ISSN 1411-9420 /e-ISSN 2460-1578) - Chemistry Department, Universitas Gadjah Mada, Indonesia.

Web Analytics View The Statistics of Indones. J. Chem.