Microwave-Assisted Preparation of Zinc-Doped β-Tricalcium Phosphate for Orthopedic Applications


Ali Taha Saleh(1*), Dheyaa Alameri(2)

(1) Department of Chemistry, College of Science, University of Misan, Misan, Iraq
(2) Department of Physics, College of Science, University of Misan, Misan, Iraq
(*) Corresponding Author


A novel two-step methodology delivering zinc into the structure of β-tricalcium phosphate (β-TCP) has been investigated. Incorporating wet precipitation of calcium-deficient apatite [Ca9-xZnx(HPO4)(PO4)5(OH)] (x = 0.00–1.00 mol) using a microwave-assisted process followed by two-hour calcination at 1000 °C has been conducted to generate a ratio of 1.48 of Zn doped β-TCP. The products were characterized by X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectrometer, and field emission scanning electron microscope (FESEM). Our results confirmed that the product was crystalline Zn2+-doped β-tricalcium phosphate. The incorporation of Zn+2 into the β-TCP lattice resulted in a shifting of diffraction peaks to higher 2θ values, which were attributed to the substitution of larger-sized Ca+2 ions with smaller-sized Zn2+ ions. A reduction in the intensity of the XRD peaks was also observed due to the reduction in the degree of crystallinity of the samples. Lattice parameters along the a and c-axis showed a gradual decrease in length with an increase in the amount of Zn2+ doping. This decrease was attributed to the replacement of Ca+2 ion by the smaller-sized Zn2+ ions. The microstructure of the powders consisted of microscale aggregates fused together. EDX analysis of all samples showed that the Zn2+ doping had successfully taken place and the amount of Zn2+ present in the samples was in good agreement with the theoretical values.


microwave-assisted; β-tricalcium phosphate; zinc; characterization

Full Text:

Full Text PDF


[1] Zhou, H., Agarwal, A.K., Goel, V.K., and Bhaduri, S.B., 2013, Microwave-assisted preparation of magnesium phosphate cement (MPC) for orthopedic applications: A novel solution to the exothermicity problem, Mater. Sci. Eng., C, 33 (7), 4288–4294.

[2] Taha, A., Akram, M., Jawad, Z., Alshemary, A.Z., and Hussain, R., 2017, Strontium doped injectable bone cement for potential drug delivery applications, Mater. Sci. Eng., C, 80, 93–101.

[3] Gozalian, A., Behnamghader, A., Daliri, M., and Moshkforoush, A., 2011, Synthesis and thermal behavior of Mg-doped calcium phosphate nanopowders via the sol gel method, Sci. Iran., 18 (6), 1614–1622.

[4] Torres, P.M.C., Gouveia, S., Olhero, S., Kaushal, A., and Ferreira, J.M.F., 2015, Injectability of calcium phosphate pastes: Effects of particle size and state of aggregation of β-tricalcium phosphate powders, Acta Biomater., 21, 204–216.

[5] Zhang, J., Liu, W., Schnitzler, V., Tancret, F., and Bouler, J.M., 2014, Calcium phosphate cements for bone substitution: Chemistry, handling, and mechanical properties, Acta Biomater., 10 (3), 1035–1049.

[6] Saleh, A.T., Ling, L.S., and Hussain, R., 2016, Injectable magnesium-doped brushite cement for controlled drug release application, J. Mater. Sci., 51 (16), 7427–7439.

[7] Zhao, J., Zhao, J., Chen, J.H., Wang, X.H., Han, Z., and Li, Y., 2014, Rietveld refinement of hydroxyapatite, tricalcium phosphate and biphasic materials prepared by solution combustion method, Ceram. Int., 40 (2) 3379–3388.

[8] Xu, H.H.K., Carey, L.E., Simon, C.G., Takagi, S., and Chow, L.C., 2007, Premixed calcium phosphate cements: Synthesis, physical properties, and cell cytotoxicity, Dent. Mater., 23 (4), 433–441.

[9] Forouzandeh, A., Hesaraki, S., and Zamanian, A., 2014, The releasing behavior and in vitro osteoinductive evaluations of dexamethasone-loaded porous calcium phosphate cements, Ceram. Int., 40 (1, Part A), 1081–1091.

[10] Ribeiro, G.B.M., Trommer, R.M., dos Santos, L.A., and Bergmann, C.P., 2011, Novel method to produce β-TCP scaffolds, Mater. Lett., 65 (2), 275–277.

[11] Ma, H., Feng, C., Chang, J., and Wu, C., 2018, 3D-printed bioceramic scaffolds: From bone tissue engineering to tumor therapy, Acta Biomater., 79, 37–59.

[12] Han, B., Ma, P.W., Zhang, L.L., Yin, Y.J., Yao, K.D., Zhang, F.J., Zhang, Y.D., Li, X.L., and Nie, W., 2009, β-TCP/MCPM-based premixed calcium phosphate cements, Acta Biomater., 5 (8), 3165–3177.

[13] Pina, S., Torres, P.M.C., and Ferreira, J.M.F., 2010, Injectability of brushite-forming Mg-substituted and Sr-substituted α-TCP bone cements, J. Mater. Sci. - Mater. Med., 21 (2), 431–438.

[14] Yashima, M., Sakai, A., Kamiyama, T., and Hoshikawa, A., 2003, Crystal structure analysis of β-tricalcium phosphate Ca3(PO4)2 by neutron powder diffraction, J. Solid State Chem., 175 (2), 272–277.

[15] Carrodeguas, R.G., and De Aza, S., 2011, α-Tricalcium phosphate: Synthesis, properties, and biomedical applications, Acta Biomater., 7 (10), 3536–3546.

[16] Cacciotti, I., and Bianco, A., 2011, High thermally stable Mg-substituted tricalcium phosphate via precipitation, Ceram. Int., 37 (1), 127–137.

[17] Kannan, S., Goetz-Neunhoeffer, F., Neubauer, J., Pina, S., Torres, P.M.C., and Ferreira, J.M.F., 2010, Synthesis and structural characterization of strontium- and magnesium-co-substituted β-tricalcium phosphate, Acta Biomater., 6 (2), 571–576.

[18] Tamimi, F., Sheikh, Z., and Barralet, J., 2012, Dicalcium phosphate cements: Brushite and monetite, Acta Biomater., 8 (2), 474–487.

[19] Razali, N.N., and Sopyan, I., 2018, Incorporation of poly(vinyl alcohol) for the improved properties of hydrothermal derived calcium phosphate cements, Indones. J. Chem., 18 (2), 354–361.

[20] Alshemary, A.Z., Goh, Y.F., Shakir, I., and Hussain, R., 2015, Synthesis, characterization and optical properties of chromium doped β-Tricalcium phosphate, Ceram. Int., 41 (1, Part B), 1663–1669.

[21] Zhang, S., Zhang, X., Cai, Q., Wang, B., Deng, X., and Yang, X., 2010, Microfibrous β-TCP/collagen scaffolds mimic woven bone in structure and composition, Biomed. Mater., 5 (6), 065005.

[22] Tao, J., Pan, H., Zhai, H., Wang, J., Li, L., Wu, J., Jiang, W., Xu, X., and Tang, R., 2009, Controls of tricalcium phosphate single-crystal formation from its amorphous precursor by interfacial energy, Cryst. Growth Des., 9 (7), 3154–3160.

[23] Shayegan, A., Petein, M., and Vanden Abbeele, A., 2009, The use of beta-tricalcium phosphate, white MTA, white Portland cement and calcium hydroxide for direct pulp capping of primary pig teeth, Dent. Traumatol., 25 (4), 413–419.

[24] Gbureck, U., Barralet, J.E., Spatz, K., Grover, L.M., and Thull, R., 2004, Ionic modification of calcium phosphate cement viscosity. Part I: Hypodermic injection and strength improvement of apatite cement, Biomaterials, 25 (11), 2187–2195.

[25] Torres, P.M.C., Abrantes, J.C.C., Kaushal, A., Pina, S., Döbelin, N., Bohner, M., and Ferreira, J.M.F., 2016, Influence of Mg-doping, calcium pyrophosphate impurities and cooling rate on the allotropic α ↔ β-tricalcium phosphate phase transformations, J. Eur. Ceram. Soc., 36 (3). 817–827.

[26] Dong, L., He, G., and Deng, C., 2016, Effects of strontium substitution on the phase transformation and crystal structure of calcium phosphate derived by chemical precipitation, Ceram. Int., 42 (10), 11918–11923.

DOI: https://doi.org/10.22146/ijc.55931

Article Metrics

Abstract views : 2952 | views : 2139

Copyright (c) 2020 Indonesian Journal of Chemistry

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.


Indonesian Journal of Chemistry (ISSN 1411-9420 /e-ISSN 2460-1578) - Chemistry Department, Universitas Gadjah Mada, Indonesia.

Analytics View The Statistics of Indones. J. Chem.