Characterization of Semi-Interpenetrated Network Alginate/Gelatin Wound Dressing Crosslinked at Sol Phase

Dian Pribadi Perkasa(1*), Erizal Erizal(2), Tri Purwanti(3), Alva Edy Tontowi(4)

(1) Department of Radiation Processing, Center for Application of Isotopes and Radiation, National Nuclear Energy Agency
(2) Department of Radiation Processing, Center for Application of Isotopes and Radiation, National Nuclear Energy Agency
(3) Department of Work Safety and Mining Installation, Center for Nuclear Ore Technology, National Nuclear Energy Agency
(4) Department of Mechanical and Industrial Engineering, Faculty of Engineering, Universitas Gadjah Mada
(*) Corresponding Author


Gel contraction of alginate during ionic crosslinking at sol phase was reduced by blending with gelatin solution due to intermolecular interaction and chain entanglement. The semi-interpenetrated network (semi-IPN) of wound dressing hydrogels were prepared by overlaid alginate/gelatin blend with 1.0% (w/w) CaCl2 solution under ambient temperature for 2 h. Results showed that gel contraction was significantly reduced with increasing gelatin content i.e. from 40.5 ± 5.8% for pure alginate to as low as 5.8 ± 1.2% for alginate/gelatin of 1:7 (w/w). It seems that gelatin successfully inhibited alginate chains mobility during their network re-arrangement by Ca2+ cation. The FTIR spectra of hydrogels showed combination of characteristic vibration of alginate and gelatin. Increasing gelatin content also significantly improved elasticity and tensile strength at break of dried hydrogels. Swelling kinetics of dried hydrogels were fitted Schott’s second-order power-law model. Increasing gelatin fraction increased the swelling rate while decreased the swelling at equilibrium. Their absorptive capacity were of interval for management of moderate to heavily exudating wound.


alginate/gelatin; wound dressing; gel contraction; swelling kinetic; biomedical engineering

Full Text:

Full Text PDF


[1] Madaghiele, M., Demitri, C., Sannino, A., and Ambrosio, L., 2014, Polymeric hydrogels for burn wound care: Advanced skin wound dressings and regenerative templates, Burns Trauma, 2 (4), 153–161.

[2] Lee, K.Y., and Mooney, D.J., 2012, Alginate: Properties and biomedical applications, Prog. Polym. Sci., 37 (1), 106–126.

[3] Saarai, A., Kasparkova, V., Sedlacek, T., and Saha, P., 2013, On the development and characterisation of crosslinked sodium alginate/gelatine hydrogels, J. Mech. Behav. Biomed. Mater., 18, 152–166.

[4] Yang, D., and Jones, K.S., 2009, Effect of alginate on innate immune activation of macrophages, J. Biomed. Mater. Res. Part A, 90 (2), 411–418.

[5] Borgogna, M., Skjåk-Bræk, G., Paoletti, S., and Donati, I., 2013, On the initial binding of alginate by calcium ions. The tilted egg-box hypothesis, J. Phys. Chem. B, 117 (24), 7277–7282.

[6] Li, J., He, J., Huang, Y., Li, D., and Chen, X., 2015, Improving surface and mechanical properties of alginate films by using ethanol as a co-solvent during external gelation, Carbohydr. Polym., 123, 208–216.

[7] Yajima, Y., Yamada, M., Yamada, E., Iwase, M., and Seki, M., 2014, Facile fabrication processes for hydrogel-based microfluidic devices made of natural biopolymers, Biomicrofluidics, 8 (2), 24115.

[8] Davidovich-Pinhas, M., and Bianco-Peled, H., 2010, A quantitative analysis of alginate swelling, Carbohydr. Polym., 79 (4), 1020–1027.

[9] Bajpai, M., Shukla, P., and Bajpai, S.K., 2017, Enhancement in the stability of alginate gels prepared with mixed solution of divalent ions using a diffusion through dialysis tube (DTDT) approach, J. Macromol. Sci. Part A Pure Appl. Chem., 54 (5), 301–310.

[10] Perkasa, D.P., Erizal, Darmawan, and Rasyid, A., 2013, Effect of gamma irradiation on mechanical and thermal properties of fish gelatin film isolated from lates calcarifer scales, Indones. J. Chem., 13 (1), 28–35.

[11] Ayvazyan, A., Morimoto, N., Kanda, N., Takemoto, S., Kawai, K., Sakamoto, Y., Taira, T., and Suzuki, S., 2011, Collagen-gelatin scaffold impregnated with bFGF accelerates palatal wound healing of palatal mucosa in dogs, J. Surg. Res., 171 (2), 247–257.

[12] Rosellini, E., Cristallini, C., Barbani, N., Vozzi, G., and Giusti, P., 2009, Preparation and characterization of alginate/gelatin blend films for cardiac tissue engineering, J. Biomed. Mater. Res. Part A, 91 (2), 447–453.

[13] Mohanan, A., and Vishalakshi, B., 2009, Swelling and diffusion characteristics of interpenetrating network films composed of sodium alginate and gelatin: Transport of Azure B, Int. J. Polym. Mater., 58 (11), 561–580.

[14] ASTM D2857-16, Standard Practice for Dilute Solution Viscosity of Polymers, 2016, ASTM International, West Conshohocken, PA.

[15] ASTM F2027-16, Standard Guide for Characterization and Testing of Raw or Starting Materials for Tissue-Engineered Medical Products, 2014, ASTM International, West Conshohocken, PA.

[16] Masuelli, M.A., 2014, Mark-Houwink Parameters for aqueous-soluble polymers and biopolymers at various temperatures, J. Polym. Biopolym. Phys. Chem., 2 (2), 37–43.

[17] ASTM D882-12, Standard Test Method for Tensile Properties of Thin Plastic Sheeting, 2012, ASTM International, West Conshohocken, PA.

[18] BS EN 13726-1:2002, Test Methods for Primary Wound Dressings. Aspects of Absorbency, 2002, British Standard Institution, London.

[19] Pamies, R., Schmidt, R.R., Martínez, M.C.L., and de la Torre, J.G., 2010, The influence of mono and divalent cations on dilute and non-dilute aqueous solutions of sodium alginates, Carbohydr. Polym., 80 (1), 248–253.

[20] Daemi, H., and Barikani, M., 2012, Synthesis and characterization of calcium alginate nanoparticles, sodium homopolymannuronate salt and its calcium nanoparticles, Sci. Iran., 19 (6), 2023–2028.

[21] Xiao, Q., Gu, X., and Tan, S., 2014, Drying process of sodium alginate films studied by two-dimensional correlation ATR-FTIR spectroscopy, Food Chem., 164, 179–184.

[22] Sarker, B., Singh, R., Silva, R., Roether, J.A., Kaschta, J., Detsch, R., Schubert, D.W., Cicha, I., and Boccaccini, A.R., 2014, Evaluation of fibroblasts adhesion and proliferation on alginate-gelatin crosslinked hydrogel, PLoS One, 9 (9), 1–12.

[23] Vidal, B.C., and Mello, M.L.S., 2011, Collagen type I amide I band infrared spectroscopy, Micron, 42 (3), 283–289.

[24] Adderley, U.J., 2010, Managing wound exudate and promoting healing, Br. J. Community Nurs., 15 (3), S15–6.

[25] Uzun, M., Anand, S.C., and Shah, T., 2013, In vitro characterisation and evaluation of different types of wound dressing materials, J. Biomed. Eng. Technol., 1 (1), 1–7.

[26] Ganji, F., Vasheghani-Farahani, S., and Vasheghani-Farahani, E., 2010, Theoretical description of hydrogel swelling: A review, Iran. Polym. J., 19 (5), 375–398.

[27] Siepmann, J., and Peppas, N.A., 2001, Modeling of drug release from delivery systems based on hydroxypropyl methylcellulose (HPMC), Adv. Drug Delivery Rev., 48 (2-3), 139–157.

[28] Schott, H., 1992, Kinetics of swelling of polymers and their gels, J. Pharm. Sci., 81 (5), 467–470.

[29] Qiao, C., and Cao, X., 2014, Swelling behavior of physically cross-linked gelatin gels in varied salt solutions, J. Macromol. Sci. Part B Phys., 53 (10), 1609–1620.

[30] Martínez-Ruvalcaba, A., Sánchez-Díaz, J.C., Becerra, F., Cruz-Barba, L.E., and González-Álvarez, A., 2009, Swelling characterization and drug delivery kinetics of polyacrylamide-co-itaconic acid/chitosan hydrogels, eXPRESS Polym. Lett., 3 (1), 25–32.

[31] Liu, J., Li, Q., Su, Y., Yue, Q., and Gao, B., 2014, Characterization and swelling-deswelling properties of wheat straw cellulose based semi-iPNS hydrogel, Carbohydr. Polym., 107, 232–240.


Article Metrics

Abstract views : 150 | views : 175


  • There are currently no refbacks.

Copyright (c) 2018 Indonesian Journal of Chemistry

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Indones. J. Chem. indexed by:

ISSN 1411-9420 (Print), ISSN 2460-1578 (online).

Analytics View The Statistics of Indones. J. Chem.