Pengaruh Radiasi UV Buatan Terhadap Kerusakan Permukaan Bahan Isolasi Resin Epoksi Silane

  • Yanolanda Suzantry H Universitas Gadjah Mada
  • Suharyanto Universitas Gadjah Mada
Keywords: Sinar UV, Sudut Kontak, Luas Kerusakan Permukaan, silane, pasir silika

Abstract

Polymer is now developed as the material replacement of the porcelain isolator and glass insulators. However, tropical climates and high rainfall can cause problems to its. Ultraviolet radiation will continuously accelerate to the surface of the polymer insulator material. As a result, the surface of the insulating material becomes easier letting electric current flow and a fast formation of extensive damage to the surface of the insulator material. Materials used in this study were made from epoxy resin diglycidyl ether of bisphenol-A (DGEBA) as the base material, metaphenylen diamine (MPDA) as the reinforcement material and silica sand. DGEBA and MPDA composition was 30% silica sand filler 30%, 25%, 20%, 15%, 10% and 10% silicone rubber was 15%, 20%, 25%, 30%. The size of the test material was 120 mm x 50 mm x 5 mm. The study was conducted in the laboratory according to standard IEC 587: 1984. This study was conducted to determine the effect of ultraviolet radiation on hydrophobic contact angle and surface damage on the broad value of insulation material epoxy resin silanes. The results showed that the length of exposure time to UV light tended to increase the value of the contact angle. This was due to exposure to artificial UV rays which would accelerate the degradation process. The longer the level of ultraviolet radiation on the sample accelerating the degradation off silane epoxy resin insulators in addition, it caused greater leakage current on extensive damage to the surface of the insulating material.

References

Berahim, Hamzah, “Metodologi Untuk Mengkaji Kinerja Isolasi Polimer Resin Epoksi Silane Sebagai Material Isolator Tegangan Tinggi di Daerah Tropis”, Disertasi,Universitas Gadjah Mada, Yogyakarta, 2005.

Wahada, Giyarhadi, “Pengaruh Sinar Ultraviolet Terhadap BahanIsolasi Resin Epoksi Dengan Pengisi Pasir Silica Dan Lem Silicone Rubber Terkontaminasi Polutan Parangtritis”, Tugas Akhir, Jurusan Teknik Elektro Fakultas Teknik UGM, Yogyakarta, 2003.

Hakim, Muhammad Arief Rahman, “Studi Pengaruh UV Terhadap Karakteristik Bahan Isolasi Resin Epoksi Berpolutan Garam (NaCl) Dengan Bahan Pengisi Pasir Silika Dan Lem Silikon”, Tugas Akhir, Jurusan Teknik Elektro Fakultas Teknik UGM, Yogyakarta, 2003.

Syakur, Abdul., Anggraini, Ika Novia., Sarjiyah., Hamzah Berahim, “Pengaruh Komposisi Bahan Isolasi Resin Epoksi dengan Bahan Pengisi Silicone Rubber terhadap Proses Tracking dan Erosi”, Universitas Gadjah Mada, Yogyakarta, 2010.

BS 5604:1986, IEC 587:1984, “Methods for Evaluating resistance to tracking and erosion of electrical insulating materials used under severe ambient conditions”, British Standards Institution, British standard (BS).

Hakim, Muhammad Arief Rahman, “Electrical Degradation and Breakdown I Polymer, IEE Material and Device Series”, England, 2003.

Nurlailati, Abdul Syakur, Sarjiya, Hamzah Berahim, Relationship Between Contact Angle and Stoichiometry Value On Epoxy Resin Polymer Insulating Materials, CTEE, Universitas Gadjah Mada, Yogyakarta, 2010.

Lee, Henry, Kris Neville, Epoxy Resins Their Applications And Technology, McGraw-Hill Book Company, INC, Newyork Torondo London, 1957.

Tobing, Bonggas L., Peralatan Tegangan Tinggi, PT. Gramedia Pustaka Utama, Jakarta, 2003.

Arismunandar A., Teknik Tegangan Tinggi, Pradnya Paramita, Jakarta., 1984.

How to Cite
Yanolanda Suzantry H, & Suharyanto. (1). Pengaruh Radiasi UV Buatan Terhadap Kerusakan Permukaan Bahan Isolasi Resin Epoksi Silane. Jurnal Nasional Teknik Elektro Dan Teknologi Informasi, 2(4), 299-306. Retrieved from https://jurnal.ugm.ac.id/v3/JNTETI/article/view/3120
Section
Articles