Development and Characterization of Three-Dimensional Lattice Hydroxyapatite Scaffolds Using Aqueous Based Extrusion Fabrication (ABEF) for Biomedical Applications

https://doi.org/10.22146/jmpc.68283

Muhammad Kusumawan Herliansyah(1*), Y Nugroho(2)

(1) Department of Mechanical and Industrial Engineering, Faculty of Engineering, Universitas Gadjah Mada. Jl. Grafika 2, Yogyakarta 55281, Indonesia
(2) Technical Academy of Industrial Engineering, Polytechnic, Surakarta, Indonesia
(*) Corresponding Author

Abstract


A solid freeform fabrication technique, aqueous based extrusion fabrication (ABEF), was investigated for the creation of three-dimensional lattice Hydroxyapatite scaffolds with pre-designed pore properties. An aqueous based Hydroxyapatite paste was extruded through a 0.8 mm nozzle, and deposited layer-by-layer at room temperature according to a computer-aided design (CAD) file. The morphology of green body and sintered body were characterized using digital microscope. The phase purity was analyzed using XRD. Fourier transform infrared spectroscopy (FTIR) was performed in order to understand the phase changes upon heating process and to determine HA stoichiometry. The current investigation confirms the possibility of producing three-dimensional lattice Hydroxyapatite scaffolds without any impurities as indicated by XRD and FTIR techniques. The morphology analysis of the structured macroporous Hydroxyapatite bioceramic shows interconnected macro pores and micro pores. It will give possibility for colonization of osteoblast in the pores, fibrovascular ingrowth and finally the deposition of new bone formation.

Keywords


Extrusion, Three-dimensional lattice, Hydroxyapatite, Biomedical Application.

Full Text:

PDF


References

A. J. Salgado, O. P. Coutinho, and R. L. Reis, Bone tissue engineering: state of the art and future trends, Macromol. Biosci., vol. 4, pp. 743-765, 2004

B.S. Chang, C.K. Lee, K.S. Hong, H.J. Youn, H.S. Ryu, S.S. Chung and K.W. Park, Osteoconduction at porous hydroxyapatite with various pore configurations, Biomaterials, vol. 21, pp. 1291-1298, 2000

H. Yoshikawa and A. Myoui, Bone tissue engineering with porous hydroxyapatite ceramics, J. Artif. Organs., vol. 8, pp. 131-136, 2005

I. Sopyan, M. Mel, Ramesh S. and K.A. Khalid, Porous hydroxyapatite for artificial bone applications, Science and Technology of Advanced Materials, vol. 8, pp. 116-123, 2007

J. Ma, C. Wang and K.W. Peng, Electrophoretic deposition of porous hydroxyapatite scaffold, Biomaterials vol. 24, pp. 3505-3510, 2003

J.A. Toque, M.K. Herliansyah, M. Hamdi, A. Ide-Ektessabi and I. Sopyan, Adhesion failure behavior of sputtered calcium phosphate thin film coatings evaluated using microscratch testing, Journal of the Mechanical Behavior of Biomedical Materials, 3, pp. 324-330, 2010

J.C. LeHuec, T. Schaeverbeke, D. Clement, J. Faber and A. LeRebeller, Influence of porosity on the mechanical resistance of hydroxyapatite ceramics under compressive stress, Biomaterials, vol. 16, pp. 113-118, 1995

J.H.G. Rocha, A.F. Lemos, S. Kannan, S. Agathopoulos and J.M.F. Ferreira, Hydroxyapatite scaffolds hydrothermally grown from aragonitic cuttlefish bones, J. Mater. Chem., vol. 15, pp. 5007–5011, 2005

J.S. Woyansky, C.E. Scott and W.P. Minnear, Processing of porous ceramics, Am. Ceram. Soc. Bull. Vol. 71, pp. 1674-1682, 1992

Karimzadeh, M.R. Ayatollahi, A.R. Bushroa and M.K. Herliansyah, Effect Of Sintering Temperature on Mechanical And Tribological Properties of Hydroxyapatite Measured by Nanoindentation and Nanoscratch Experiments, Ceramics International,vol 40, pp. 9159-9164, 2014

L.M. Rodriguez-Lorenzo and J.M.F. Ferreira, Development of porous ceramic bodies for application in tissue engineering and drug delivery systems. Mater. Res. Bull., vol. 39, pp. 83-91, 2004

L.M. Rodriguez-Lorenzo, M. Vallet-Regi and J.M.F. Ferreira, Fabrication of porous hydroxyapatite bodies by a new direct consolidation method: starch consolidation, J. Biomed. Mater. Res., vol. 60, pp. 232-240, 2002a

L.M. Rodriguez-Lorenzo, M. Vallet-Regi and J.M.F. Ferreira, Fabrication of Hydroxyapatite Bodies by Uniaxial Pressing from a Precipitated Powder. Biomaterials, vol. 22, pp. 583-588, 2001

L.M. Rodriguez-Lorenzo, M. Vallet-Regi, J.M.F. Ferreira, M.P. Ginebra, C. Aparicio and J. Planell, A Hydroxyapatite Ceramic Bodies with Tailored Mechanical Properties for Different Applications, J. Biomed. Mat. Res., vol. 60, pp. 159-166, 2002

M. Itokazu, Y. Wenyi, T. Aoki, A. Ohara and N. Kato, Synthesis of antibiotic-loaded interporous hydroxyapatite blocks by vacuum method and in vitro drug release testing, Biomaterials, vol. 19, no. 7-9, pp. 817-819, 1998

M. Otsuka, Y. Nakahigashi, Y. Matsuda, J.L. Fox, W.I. Higuchi and Y. Sugiyama, A novel skeletal drug delivery system using self-setting calcium phosphate cement VIII: the relationship between in vitro and in vivo drug release from indomethacin-containing cement, Journal of Controlled Release, vol. 43, pp. 115–122, 1997

M.K. Herliansyah, M. Hamdi, A. Ide-Ektessabi, M.W. Wildan and J.A. Toque, The Influence of Sintering Temperature on the Properties of Compacted Bovine Hydroxyapatite, Materials Science And Engineering: C, vol. 29, pp. 1674-1680, 2009

M.K. Herliansyah, Suyitno, P. Dewo, M. Hamdi, and A. Ide-Ektessabi, Development And Characterization of Bovine Hydroxyapatite Porous Bone Graft For Biomedical Applications, Advanced Materials Research Vol. 277, pp 59-65, 2011

N. Tamai, A. Myoui, T. Tomita, T. Nakase, J. Tanaka, T. Ochi and H. Yoshikawa, Novel hydroxyapatite ceramics with an interconnective porous structure exhibit superior osteoconduction in vivo, J. Biomed. Mater. Res. Vol. 59, pp. 110-117, 2002

NIST, Certificate of Analysis – Standard Reference Material 2910: Calcium Hydroxyapatite, National Institute of Standard & Technology. 1997

O. Gauthier, J. Bouler, E. Aguado, P. Pilet and G. Daculsi, Macroporous biphasic calcium phosphate ceramics: influence of macropore diameter and macroporosity percentage on bone ingrowth, Biomaterials, vol. 19, pp. 133-139, 1998

S. Guicciardi, C. Galassi, E. Landi, A. Tampieri, K. Satou and G. Pezzoti, Rheological characteristics of slurry controlling the microstructure and the compressive strength behavior of biomimetic hydroxyapatite, J. Mater. Res. Vol.16, pp. 163-170, 2001

S. Joschek, B. Nies, R. Krotz and A. Gopfrerich, Chemical and physicochemical characterization of porous hydroxyapatite ceramics made of natural bone, Biomaterials vol. 21, pp. 1645-1658, 2000

S. Pramanik, A.K. Agarwaly and K.N. Rai, Development of High Strength Hydroxyapatite for Hard Tissue Replacement, Trends Biomater. Artif. Organs, vol. 19 no. 1, pp. 46-51, 2005

S.F. Hulbert, S.J. Morisson and J.J. Klawitter, Tissue reaction to three ceramics of porous and non-porous structures, J. Biomed. Mater. Res., vol. 6, pp. 347-374, 1972

T.J. Flatley, K.L. Lynch and M. Benson, Tissue Response to Implants of Calcium Phosphate Ceramic in the Rabbit Spine, Clin. Orthop., vol 179, pp. 246-252, 1983

Y. Fang, D.K. Agarwal, D.M. Roy and R. Roy, Fabrication of porous hydroxyapatite ceramics by microwave processing, J. Mater. Res. Vol. 7, pp. 490-494, 1992

Y. Suzuki, S. Matsuya, K. Udoh and M. Nakagawa, Fabrication of hydroxyapatite block from gypsum block based on (NH4)2HPO4 treatment, Dental Materials Journal,vol. 24,pp. 515-521, 2005



DOI: https://doi.org/10.22146/jmpc.68283

Article Metrics

Abstract views : 1090 | views : 796

Refbacks

  • There are currently no refbacks.