Research article

Vol 8 No 2 (2014): Volume 8, Number 2, 2014

Sintesis ZSM-5 dari coal fly ash (CFA) dengan sumber silika penambah yang berasal dari abu sekam padi: pengaruh rasio SiO2/Al2O3 terhadap kristalinitas produk

DOI
https://doi.org/10.22146/jrekpros.11374
Submitted
November 15, 2023
Published
December 31, 2014

Abstract

Coal Fly Ash and rice husk ash can be utilized by converting it into ZSM-5 synthetic zeolite. One of the influencing factors of ZSM-5 synthetis is ratio of SiO2/Al2O3. Synthesis of ZSM-5 was carried out in an autoclave at a temperature of 180°C with a variation of the ratio of SiO2/Al2O3, namely 20, 30, 40, 50 and 60 mol/mol during 24 hour crystallization using TPABr template. Characterization of ZSM-5 was conducted using X-ray Diffraction, Scanning Electron Microscopy, Adsorption-Desorption Analysis of Nitrogen and Acidity. The results showed that the ZSM-5 was formed in all the variations of SiO2/Al2O3 ratios with the highest percent crystallinity of 52.83%, at the ratio of 50 mol/mol. All products are still in accompany with the formation of side products such as Analsime and Silica Oxide. The ZSM-5 crystal product was in hexagonal shape. Results from Adsorption-Desorption Analysis of Nitrogen indicated that all products were mesoporous materials.

References

  1. Chareophanic,M., Teerapong Namto., Paisan K. and Jumras L. 2003. Synthesis of ZSM-5 zeolite from lignite fly ash and rice husk ash. Bangkok : Kasetsart University
  2. Damayanti,T. 2012. Penentuan Rasio SiO2/Al2O3 terbaik Pada Sintesis ZSm-5 Dari Zeolit Alam Lampung Dengan Sumber Silika Penambah Abu Sekam Padi. Universitas Lampung : Bandar Lampung
  3. Hadi, S.K. 1993. Pembuatan dan Karakterisasi Zeolit A dari Sekam Padi, Skripsi 86/57716/PA/3926. UGM: Yogyakarta.
  4. Laksono,A dan Prasetyoko,D. 2007. Abu Sekam Padi Sebagai Sumber Silika Pada Sintesis Zeolit ZSM-5 Tanpa Menggunakan Templat Organik. Akta Kimia Indonesia Vol.3: Surabaya.
  5. Nurjannah, Irmawati., Roesyadi,A., dan Danawati. 2010. Perengkahan Katalitik Asam Oleat Untuk Menghasilkan Biofuel Menggunakan HZSM-5 Sintesis. Teknik Kimia FTI : ITS
  6. Prijatama,H. 1996. Abu Terbang dan Pemanfaatannya. Seminar Nasional Pemanfaatan Energi Batu bara. Pulitbang Geoteknologi LIPI: Serpong.
  7. Purnamasari,I dan Prasetyoko,D. 2010. Sintesis & Karakterisasi ZSM-5 Mesopori serta Uji Aktivitas Katalitik pada Reaksi Esterifikasi Asam Lemak Stearin Kelapa Sawit. FMIPA : ITS.
  8. PLTU Tarahan. 2010. Data Pusat penelitian dan pengembangan teknologi mineral dan Batu bara sample CFA jenis lignit dan sub-bituminos PT. PLN sektor Pembangkitan Tarahan. Lampung
  9. Rahmawati,Z., dan Prasetyoko,D. 2009. Sintesis TS-1 Mesopori Menggunakan Prekursor dengan Variasi Waktu Hidrotermal. Kimia MIPA : ITS.
  10. Rodiansono,Trisunaryanti,M., dan Triyono. 2007. Pembuatan, Karakterisasi dan Uji Aktivitas Katalis NiMo/Z dan NiMo/Z-Nb2O5 pada Reaksi Hidrorengkah Fraksi Sampah Plastik menjadi Fraksi Bensin. Jurnal Berkala MIPA: Universitas Lambung Mangkurat.
  11. Setiadi,S., dan Pertiwi,A. 2007. Preparasi dan Karakterisasi Zeolit Alam untuk Konversi Senyawa Abe menjadi Hidrokarbon. Prosiding Kongres dan Simposium Nasional.
  12. Setiadi, S., dan Nasikin,M. 2011. Study on Crystallization Stage for ZSM-5 preparation. International QIR, Bali
  13. Tim Redaksi. 2010. Ragam Pemanfaatan Limbah Padat Pembangkitan. Tanjung Jati. April 2010.
  14. Yusri, Silvia. 2012. Sintesis dan Karakterisasi Zeolit ZSM-5 Mesopori dengan Secondary Template dan Studi Awal Katalisis Oksidasi Metana. FMIPA: UI.