Effect of Venting on the Explosion of AluminiumSilver Powder Mixture

  • Khairiah Mohd Mokhtar Department of Chemical Engineering, Faculty of Engineering, University of Malaya, 50603, Kuala Lumpur
  • Che Rosmani Che Hassan Department of Chemical Engineering, Faculty of Engineering, University of Malaya, 50603, Kuala Lumpur
  • Rafiziana Md Kasmani Department of Energy Engineering, School of Chemical and Energy Engineering, Universiti Teknologi Malaysia, Johor, 81310, Malaysia
  • Mahar Diana Hamid Department of Chemical Engineering, Faculty of Engineering, University of Malaya, 50603, Kuala Lumpur
  • Mohamad Iskandr Mohamad Nor Department of Chemical Engineering, Faculty of Engineering, University of Malaya, 50603, Kuala Lumpur
  • Mohd Usman Mohd Junaidi Department of Chemical Engineering, Faculty of Engineering, University of Malaya, 50603, Kuala Lumpur
Keywords: Explosion characteristics, Nanoaluminium, Nanosilvet, Static burst pressure, Venting

Abstract

Dust explosion is considered as a serious threat for the industry that use or handle combustible materials as it may lead towards a significant economic loss in terms of damage to the facilities and suspension of activities, severe workplace injuries and fatalities. The rapid pressure developed during a dust explosion can be mitigated by venting. The present work explored the effects of venting on the explosion of different mixing weight ratios of aluminium and silver powder mixtures. The explosion characteristics of aluminium-silver mixtures were assessed in a 0.0012 m3 confined and vented cylindrical vessel. It was found that the application of 0.1 bar static burst pressure (Pstat) venting membrane gives one tenth reduction on explosion pressure and maximum rate of pressure rise for 70:30 and 50:50 mixing weight ratios of aluminium-silver mixtures explosion, respectively. This finding suggests that besides the venting application effect, the oxidation reaction of aluminium could be disrupted due to the presence of silver powder in the metal mixtures which results in lower heat transfer and reduction of the mass burning rate, hence, lessen flame speeds and explosion severity. However, the venting effectiveness is reduced when the Pstat increases. In order to assess the applicability of the dust explosion venting standard; NFPA 68 and EN 14491, the experimental results were compared with the calculated values according to the standards. The comparative results show that, both NFPA 68 and EN 14491 give underestimated values for explosion venting as compared with the experimental results.

References

1. Boilard, S.P., Amyotte, P.R., Khan, F.I., Dastidar, A.G., Eckhoff, R.K. (2013). “Explosibility of micron-and nano-size titanium powders,” J. Loss Prev. Process Ind., 39, 121-30.
2. CSB, CSB Investigation Report, Combustible Dust Hazard Study 2010.
3. Dufaud, O., Traoré, M., Perrin, L., Chazelet, S., Thomas, D. (2010). “Experimental investigation and modelling of aluminum dusts explosions in the 20 L sphere J. Loss Prev. Process Ind., 23(2), 226-36.
4. Dust explosion venting protective systems BS EN 14491:2012, 2012 ed. BSI.
5. Gao, W., Yu, J., Zhang, X., Li, J., Wang, B. (2015). “Characteristics of vented nano-polymethyl methacrylate dust explosions,” Powder Technol., 283, 406-14.
6. Gao, W., Yu, J., Li, J., Zhang, Q., Xie, Q., Zhang, X., et al. (2016). “Experimental investigation on micro- and nano-PMMA dust explosion venting at elevated static activation overpressures,” Powder Technol., 301, 713-22.
7. Ibarreta, A.F., Myers, T.J. (2017). “Mitigating fire and explosion hazards of powdered metals,” Metal Powder Report., 72, 57-61.
8. Jiang, B., Lin, B., Shi, S., Zhu, C., Li, W. (2011). “Explosive characteristics of nanometer and micrometer aluminum-powder,” Min. Sci. Technol. (China)., 21(5), 661-666.
9. Li, Q., Lin, B., Li, W., Zhai, C., Zhu, C. (2011). “Explosion characteristics of nano-aluminum powder–air mixtures in 20 L spherical vessels,” Powder Technol.., 212(2), 303-309.
10. Li, Q., Wang, K., Zheng, Y., Mei, X., Lin, B. (2016). “Explosion severity of micro-sized aluminum dust and its flame propagation properties in 20L spherical vessel,” Powder Technol., 301(Supplement C), 299-308.
11. Li, G., Yang, H., Yuan, C., Eckhoff, R.K. (2016). “A catastrophic aluminium-alloy dust explosion in China,” J. Loss Prev. Process Ind., 39, 121-30.
12. Manju, M. (2014). “Explosion characteristics of micron- and nano-size magnesium powders,” J. Loss Prev. Process Ind., 27, 55-64.
13. Wu, H-C, Ou, H-J, Hsiao, H-C, Shih, T-S. (2010). “Explosion characteristics of aluminum nanopowders,” Aerosol Air Qual. Res., 10(1), 38-42.
14. Yan, X., & Yu, J. (2014). “Dust explosion venting of small vessels at the elevated static activation overpressure,” Powder Technol., 261, 250-256.
15. Yan, X., Yu, J., & Gao, W. (2015). “Flame behaviors and pressure characteristics of vented dust explosions at elevated static activation overpressures,” J. Loss Prev. Process Ind.. 33, 101-108.
Published
2020-06-30
How to Cite
Mokhtar, K. M., Che Hassan, C. R., Kasmani, R. M., Hamid, M. D., Mohamad Nor, M. I., & Mohd Junaidi, M. U. (2020). Effect of Venting on the Explosion of AluminiumSilver Powder Mixture. ASEAN Journal of Chemical Engineering, 20(1), 11-19. Retrieved from https://jurnal.ugm.ac.id/v3/AJChE/article/view/9094
Section
Articles